The United States imported universal M51 copper aluminum low temperature welding wire M51-F flux 179 degree electric iron can be welded

Bizbee Sourcing

Check the original link >

CNY ￥ 168.0 ≈ $ 22.9

Real-time USD to CNY exchange rate:7.3206

International shipping not included

Model:

12 m 1.3 Diameter welding wire +1 bottle of 30g flux 4 2.3 diameter welding wires +1 bottle of 30g flux M51-F a bottle of 30g flux

Quantity:

Disclaimer

All commodity information and merchants are original sources of third-party e-commerce platforms. Bizbee only provides information search and transaction services. You should verify the authenticity of the information before the entrustment of the purchase, and accept the risks of the quality of the product that may exist.

I have read the above disclaimer and your terms of service, and I agree to both.

Coming soon

Related Products

Item Details After Sales Service

O1CN01UtKuWH1e06rojIYXs_!!2210

直径2.3mm x450mm是4根焊丝配一瓶30克助焊剂.

直径1.3mm是12米焊丝配一瓶30克助焊剂

M51是WEWELDING-M51的简称，也叫万能51，是美国R&D工业公司出厂的牌号，它是一种含有特殊稀有元素的低温铜铝焊丝，主要用于在低温下解决几乎所有白色金属的显著能力，白色金属包括锌（几乎不能焊接）、铜铅合金、锡铅合金、铝和铅等。M51 还可将上述任何一种金属与铜、黄铜、钢、不锈钢或青铜等其他任何金属焊合。

M51 特性

1）在179 度的低温下焊接。

2）配合高效焊剂M51-F，流动性强，抗氧化，除油杂。

3）抗拉强度能达到13 公斤/平方毫米。

4）特别适合于铜和铝的焊接，亦可以焊接所有白色金属，及白色金属与各种铜的焊接。

5）M51焊丝使用过程中需要辅助M51-F 焊剂焊接，M51-F没有腐蚀性，焊后在温水里面用钢丝刷清洗即可。

使焊接锌压铸件简化

长期以来，人们认为锌压铸件用普通的焊条不可焊，因焊合前会引起锌压铸件下垂和踏陷。为获得最佳结果，采用M51 时需采用M51-F 焊剂。

焊接原理：

1）加热被焊母材。为了达到两种金属连接的更好效果，两种金属同时加热，但是以加热铜线为主，切忌温度不要烧高了，因为材料的熔点和焊剂的熔点才200来度，如果温度烧高了，焊剂加上去就会发黑。

2）破除金属张力。在M51-F铜铝焊剂的作用下破除金属表面的金属张力，此过程可以有两种方法，一种可以先在母材焊接处抹上少许M51-F铜铝焊剂，用多孔喷枪加热母材（注意此时千万不要用火烧到M51-F铜铝焊剂，主要靠热传导使M51-F铜铝焊剂剧烈沸腾）直至M51-F焊剂剧烈沸腾就可以下M51-F铜铝焊丝；另外一种可以先不在母材焊接处抹焊剂，可以直接加热，然后用M51铜铝焊丝沾着M51-F焊剂下铜铝焊丝于焊接处。

3）表面温度如果够的话，会成型一条非常亮白的焊缝，自然缓冷，用温水清洗表面的残留M51-F焊剂